X4317 machining, welding, PWHT and hardening

[Machinist85]

I should produse a job which contains two part of x4317 (din 1.6587) case hardening steel.

I should slip and weld a 85mm diameter/700mm long shaft to a disk plate of same material. The outer diameter of shaft would be 240mm where the thickness is 25mm. After welding, PWHT and hardening process would be done. 

Client request a geometric tolerance of 0.02 mm across the long axis and hardness of 50-55 HRC.

To meet HT distortion how much cover I should consider in machining process?

Is there any of you guys to give me some advice?

[#Rekd™]

No bid!

[GoetzInd]

Your will have to grind as assembly after weld and heat treat to achieve that runout and cylindricity on something of that size.

Mike 

[Machinist85]

Thanks for your reply, The problem are welding distortion and heat treatment  swelling. I should consider a cover size in machining step and that size should be an optimum value because of grinding cost.